J506NiCrCu  Corrosion-resistant Steel Electrode

J506NiCrCu Corrosion-resistant Steel Electrode

J506NiCrCu

J506NiCrCu
GB:GB-E5016-G
AWS:
Current:Used for welding carbon steel and 490MPa tensile strength atmospheric corrosion-resistant steel structures, such as locomotive vehicles, offshore engineering, bridges, etc.

J506NiCrCu

According with GB GB-E5016-G


Introduction: J506NiCrCu is a kind of atmospheric corrosion-resistant steel electrode with low-hydrogen potassium type coating. AC/DC. All-position welding. The weld metal has excellent atmospheric corrosion-resistance, crack-resistance, plasticity and toughness.


Uses: Used for welding carbon steel and 490MPa tensile strength atmospheric corrosion-resistant steel structures, such as locomotive vehicles, offshore engineering, bridges, etc.


Chemical Composition of Deposited Metal (%)
Chemical Composition
C
Mn
Si
S
P
Cu
Ni
Cr
Guarantee Value
≤0.12
0.30~0.90
≤0.70
≤0.030
≤0.035
0.20~0.50
0.20~0.50
0.20~0.40

Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReL或Rp0.2(Mpa)
A(%)
KV2(J)
KV2(J)
Guarantee Value
≥490
≥390
≥22
—(-30℃)
≥27(-40℃)
General Result
500~600
400~480
23~29
60~160
50~150

Diffusible Hydrogen Content in Deposited Metal: ≤6.0ml/100g(Glycerine Hydrogen Test)

X-ray Radiographic Inspection: ⅠDegree

Reference Current (AC, DC+)
Electrode Diameter(mm)
φ2.5
φ3.2
φ4.0
φ5.0
Welding Current (A)
50~90
80~130
140~190
170~230

Instructions:
1.The electrodes must be baked under about 350℃ for an hour before welding, and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before welding.
3.When welding, short arc must be used and stringer bead is suitable.