Fluorocarbon Primers & Fluorocarbon Finish

Fluorocarbon Finish(different colors) (use for bridges and steel structures)

Characteristics:excellent retention of color and gloss property、perfect resistance of elements、excellent antifouling property、 excellent adhesion with polyurethane paint and epoxy paint、 perfect resistance of oil and water、attack、abrasion property, good construction property.
Uses:widely use for bridges、highway guardrail、top quality building、oil equipment and anticorrosion of storage tank.
Technical target：
Mixing ratio: Host crystal/Firming agent=10/1(by weight)
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.09kg/ m2/30μm
Solid contents: 60%
Humidity requirement: below 85%
Drying time & Coating interval

Substrate treatment：Primer surface should be clean and dry, no feculence
Matching：
Applicable under coatings: Fluorocarbon primers

---------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------

Fluorocarbon Primers (use for bridges and steel structures)

Characteristics:excellent anticorrosion property、perfect resistance of elements、oil and water、attack、abrasion property, good construction property.
Uses:widely use for bridges、highway guardrail、top quality building、oil equipment and anticorrosion of storage tank.
Technical target：
Mixing ratio: Host crystal/Firming agent=10/1(by weight)
Standard film thickness: Dry: 40μm/coat
Academic spreading rate: 0.09kg/ m2/40μm
Solid contents: 65%
Humidity requirement: below 85%
Drying time & Coating interval

Substrate treatment：Remove rust、oxide skin by abrasive blasting,reached ISO Sa2.5 grade
Matching：
Applicable substrate: Unpainted steel
Applicable upper coatings:Fluorocarbon finish (different colors)