200℃ ~ 600℃ Organic Silicon Air Drying Finish

200℃ ~ 600℃ Organic Silicon Air Drying Finish

一, 200℃ Organic Silicon Air Drying Finish (Different Colors)

Characteristics: dry quickly, excellent physical and mechanical property、perfect heat resistance、elements resistance, good construction property.
Uses: applicable for sprayed under 200℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 25μm/coat
Academic spreading rate: 0.08kg/ m2/25μm
Solid contents: 50%
Humidity requirement: under 85%
Drying time & Coating interval

Temperature （℃）	-10	0	10	20	30
Dry to touch（hrs）	60	50	40	30	20
Dry semi-hard（hrs）	12	8	6	5	4
Min. interval（hrs）	12	8	6	5	4

Substrate treatment: Primer surface should be clean and dry, no feculence
Matching: Applicable under coatings: FX200℃ organic silicon heat resistance primers

二, 300℃Organic Silicon Air Drying Finish (Green、Black、Steel grey)

Characteristics: dry quickly, excellent physical and mechanical property、perfect heat resistance、elements resistance property, good construction property.
Uses: applicable for sprayed under 300℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 25μm/coat
Academic spreading rate: 0.08kg/ m2/25μm
Solid contents: 50.2%
Humidity requirement: under 85%
Drying time & Coating interval

Temperature （℃）	-10	0	10	20	30
Dry to touch（hrs）	60	50	40	30	20
Dry semi-hard（hrs）	12	8	6	5	4
Min. interval（hrs）	12	8	6	5	4

Substrate treatment: Primer surface should be clean and dry, no feculence
Matching: Applicable under coatings: FX400℃ organic silicon heat resistance primers

三, 400℃ Organic Silicon Air Drying Finish(Green、Black、Steel grey)

Characteristics: dry quickly, excellent physical and mechanical property、good heat resistance、elements resistance、construction property.
Uses: applicable for sprayed under 400℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.

Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 25μm/coat
Academic spreading rate: 0.08kg/ m2/25μm
Solid contents: 50.2%
Humidity requirement: below 85%
Drying time & Coating interval

Temperature （℃）	-10	0	10	20	30
Dry to touch（hrs）	60	50	40	30	20
Dry semi-hard（hrs）	12	8	6	5	4
Min. interval（hrs）	12	8	6	5	4

Substrate treatment: Primer surface should be clean and dry, no feculence
Matching : Applicable under coatings: FX400℃ organic silicon heat resistance primers

四, 600℃ Organic Silicon Air Drying Finish (Green、Black、Steel grey)

Characteristics: dry quickly, excellent physical and mechanical property、good heat resistance、elements resistance、construction property.
Uses: applicable for sprayed under 600℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 25μm
Academic spreading rate: 0.08kg/ m2/25μm
Solid contents: 50%
Humidity requirement: below 85%
Drying time & Coating interval

Temperature （℃）	-10	0	10	20	30
Dry to touch（hrs）	60	50	40	30	20
Dry semi-hard（hrs）	12	8	6	5	4
Min. interval（hrs）	12	8	6	5	4

Substrate treatment: Primer surface should be clean and dry, no feculence
Matching: Applicable under coatings: FX600℃ organic silicon heat resistance primers