JQ.H08A  Submerged-arc Welding Wire

JQ.H08A Submerged-arc Welding Wire

JQ.H08A
GB:H08A
AWS:EL8
Current:Used together with fused flux 431 or sintered fluxes 301 and 501. Used for both high speed welding and filling welding on 50kg class base metals.
Main Applications:

JQ.H08A

According with GB H08A
Corresponding with AWS EL8
JIS W11


Introduction: It is a kind of low-manganese and low-silicon type welding wire. It matches with high-manganese and high-silicon type welding flux. It is not sensitive to the rust on the base metal. It has excellent bead molding and slag detachability. It is the most frequently used submerged-arc welding wire. Monopole or dipole. AC/DC.


Uses: Used together with fused flux 431 or sintered fluxes 301 and 501. Used for both high speed welding and filling welding on 50kg class base metals.


Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Ni
Cr
≤0.10
0.3~0.55
≤0.03
≤0.030
≤0.030
≤0.30
≤0.20

Mechanical Properties of Deposited Metal
Test Items Rm ReL或Rp0.2 A KV2(J)
Flux Used Together (Mpa) (Mpa) (%) 0℃ -20℃
SJ301 415-550 ≥330 ≥22 ≥27
HJ431 415-550 ≥330 ≥22 ≥27

Wire Size
diameter(mm) φ2.5 φ3.2 φ4.0 φ5.0