Alloprene Anticorrosive Paint,Alloprene Anticorrosive Paint manufacturer. - Hi-Sea Group 
Alloprene Anticorrosive Paint

Alloprene Anticorrosive Paint

Alloprene Anticorrosive Primers(Iron Red) (use for boat)

Characteristics:excellent anticorrosive property、brine resistance property、dry quickly, good adhesion with different kinds of primers, excellent anticorrosion effects which sprayed alloprene finish, it can still constructed under -20℃.
Uses:mainly use for antirust coating of new boat or old boat waterline below and above part.
Technical target
Mixing ratio: single component
Standard film thickness: Dry: 50μm/coat
Academic spreading rate: 0.11kg/ m2/50μm
Solid contents: 65%
Humidity requirement: below 85%
Drying time & Coating interval

Temperature(℃)

-10

0

10

20

30

Dry to touch(hrs)

50

40

30

20

15

Dry semi-hard(hrs)

10

6

5

3.5

3

Min. interval(hrs)

10

6

5

3.5

3

Substrate treatment:Remove rust by abrasive blasting,reached ISO Sa2.5 grade or remove rust by hand electrically, reached St3 grade
Matching:
Applicable substrate:Unpainted steel or sprayed alloprene aluminum powder anticorrosive primers(silver)
Applicable upper coatings:Ethylene linking paint,Alloprene boot-topping paint,Alloprene anticorrosive finish(different colors)

Alloprene Anticorrosive Intermediate Paint(Gray) (Use for shipping boat、steel structure)

Characteristics:excellent anticorrosion property、shielding property、 resistance of machine abrasion property、construction property, dryquickly.
Use:mainly use for anticorrosion of new boat or old boat waterlineunder and above part, as a use of intermediate paint, also use for huge steel structure ,as a use of anticorrosive intermediate paint.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 50μm/coat
Academic spreading rate: 0.13kg/ m2/50μm
Solid contents: 65%
Humidity requirement: below 85%
Drying time & Coating interval

Temperature(℃)

-10

0

10

20

30

Dry to touch(hrs)

55

45

35

25

17

Dry semi-hard(hrs)

11

7

5.5

4

3.5

Min. interval(hrs)

11

7

5.5

4

3.5

Substrate treatment:Primer surface should be clean and dry, no feculence
Matching:
Applicable under coatings: Alloprene anticorrosive primers( iron red),Alloprene aluminum powder anticorrosive primers( silver)
Popular type alloprene anticorrosive paint,Applicable upper coatings:,Alloprene anticorrosive finish(different colors)

Alloprene Anticorrosive Finish(Different colors) (use for boat and steel structure)

Characteristics:excellent resistance of elements、resistance of brine splash property, resistance of oil、abrasion, dry quickly, applicable to different kinds of coatings matching.
Uses:mainly use for ship-building industry and anticorrosion of coastal steel structure, also use for acid factory、alkali factory etc. large steel facilities、anticorrosion of storage tank outside.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.10kg/ m2/30μm
Solid contents: 60%
Humidity requirement: below 85%
Drying time & Coating interval

Temperature(℃)

-10

0

10

20

30

Dry to touch(hrs)

60

50

40

30

20

Dry semi-hard(hrs)

12

8

6

5

4

Min. interval(hrs)

12

8

6

5

4

Substrate treatment:Primer surface should be clean and dry, no feculence
Matching:
Applicable under coatings:Popular type alloprene anticorrosive paint ,Alloprene anticorrosive intermediate paint(gray)
Alloprene aluminum powder anticorrosive primers(silver)

CONTACT WITH US NOW

Our mail: manager@hiseamarine.com

Society certificates

Hi-Sea Group-Obtained-certification