Epoxy Zinc-Rich Anticorrosive primers,Epoxy Zinc-Rich Anticorrosive primers manufacturer. - Hi-Sea Group 
Epoxy Zinc-Rich Anticorrosive primers

Epoxy Zinc-Rich Anticorrosive primers

Epoxy Zinc-Rich Anticorrosive primers


Characteristics:when the air humidity reached 94%, it can still firmed be film, cathodic protection、excellent rust resistance and anticorrosive property, quickly dry, perfect adhesion with steel surface which after abrasive blasting handle it, abrasion resistance, good attack resistance, short coating interval, excellent torch cutting and weldability property.
Uses:Mainly use for anticorrosive steel structure in South high humidity area, also use for the anticorrosion of offshore platform、new-built boats etc. in high humidity environment.


Technical target:
Mixing ratio: Host crystal/ Firming agent=10/1 (by weight)
Standard film thickness: dry: 50μm/coat
Academic spreading rate: 0.18kg/ m2/50μm
Solid contents: 80%
Humidity requirement: below 94%
Drying time & Coating interval

Temperature℃

-10

0

10

20

30

Dry to touch (hrs)

40

20

10

8

5

Dry semi-hard (hrs)

18

10

6

5

3

Min. interval (hrs)

18

12

9

6

5

Substrate treatment:Remove rust、oxide skin and shop primer by abrasive blasting, reached ISO Sa2.5 grade.
Matching:
Applicable substrate: Unpainted steel
Applicable upper coatings: Match with kinds of epoxy、polyurethane、rubber、asphalt paints.